Effect of Annealing on Structural, Textural, Thermal, Magnetic, and Luminescence Properties of Calcium Fluoride Nanoparticles

详细

Mesoporous nanocrystalline CaF₂ powder was produced by pulsed electron beam evaporation (PEBE) in vacuum. The specific surface area (SSA) of CaF₂ nanopowder (NP) reached 88.7 m²/g. The effect of in-air thermal annealing in the temperature range of 200–900°C on the particle size, morphology, textural, thermal, magnetic, and luminescence properties of NPs is studied. A strong deviation from stoichiometry is observed in produced nanoparticles and a significant increase in the SSA after annealing at 200°C. The obtained CaF₂ NP shows ferromagnetic (FM) behavior. The FM response appearance can be explained by the formation of structural and radiation defects. An analysis of pulsed cathodoluminescence (PCL) and magnetization curves of CaF₂ NPs allows conclusions about their interrelation.