Photoluminescence at the fundamental absorption edge of single-crystal silicon textured without masking
- Авторы: Emel’yanov A.M.1, Abolmasov S.N.2, Terukov E.I.1,2
-
Учреждения:
- Ioffe Physical-Technical Institute
- R&D Center for Thin-Film Technologies in Energetics
- Выпуск: Том 42, № 10 (2016)
- Страницы: 1002-1004
- Раздел: Article
- URL: https://bakhtiniada.ru/1063-7850/article/view/201569
- DOI: https://doi.org/10.1134/S1063785016100059
- ID: 201569
Цитировать
Аннотация
The extraction efficiencies of edge luminescence from single-crystal silicon have been compared for three structures: textured without masking, untextured, and textured with masking by the technology of high-efficiency solar cells. The highest efficiency was obtained for the structure textured without masking. For this structure, the efficiency of power conversion at a wavelength of ~0.66 μm and power of 75 mW into edge PL power emerging from the semiconductor was η ≈ 0.8% under the nonradiative recombination conditions described by the exponential photoluminescence (PL) decay time constant of ~0.11 ms. The directivity diagrams of the edge PL were measured for the three structures under study.
Об авторах
A. Emel’yanov
Ioffe Physical-Technical Institute
Автор, ответственный за переписку.
Email: Emelyanov@mail.ioffe.ru
Россия, St. Petersburg, 194021
S. Abolmasov
R&D Center for Thin-Film Technologies in Energetics
Email: Emelyanov@mail.ioffe.ru
Россия, St. Petersburg, 194064
E. Terukov
Ioffe Physical-Technical Institute; R&D Center for Thin-Film Technologies in Energetics
Email: Emelyanov@mail.ioffe.ru
Россия, St. Petersburg, 194021; St. Petersburg, 194064
Дополнительные файлы