IR Photodetectors Based on Isoperiodic Epitaxial Layers of Lead Tin Chalcogenides
- Autores: Tsarenko O.N.1, Tkachuk A.I.1, Ryabets S.I.1
-
Afiliações:
- Vinnichenko Central Ukrainian State Pedagogical University
- Edição: Volume 64, Nº 3 (2019)
- Páginas: 368-372
- Seção: Solid State Electronics
- URL: https://bakhtiniada.ru/1063-7842/article/view/203073
- DOI: https://doi.org/10.1134/S1063784219030253
- ID: 203073
Citar
Resumo
IR photodetectors have been made on Pb/δ-layer/p-Pb1 –xSnxTe1 –ySey/p+-Pb0.8Sn0.2Te/Au and Au/δ-layer/n-Pb1 –xSnxTe1 –ySey(BaF2)/Pb surface-barrier structures prepared by liquid-phase epitaxy and thermal evaporation. At ~170 K, peak wavelength λp ~ 7.9–8.2 μm, and cutoff wavelength λc ~ 8.2–8.5 μm, the former surface-barrier structure has product R0A (where R0 is the zero-bias differential resistance and A is the active surface area) = 0.31–0.97 Ω cm2, peak quantum efficiency ηλ = 0.32–0.48, and specific detectability \(D_{\lambda }^{*}\) = (0.72–1.83) × 1010 cm Hz1/2 W–1. For photodiodes made on the latter surface-barrier structure, these parameters measured at ~80 K are R0A = 1.71–2.72 Ω cm2, ηλ = 0.34–0.49, and \(D_{\lambda }^{*}\) = (3.02–4.51) × 1010 cm Hz1/2 W–1 at λp ~ 8.6–12.3 μm and λc ~ 9.2–12.9 μm.
Sobre autores
O. Tsarenko
Vinnichenko Central Ukrainian State Pedagogical University
Autor responsável pela correspondência
Email: olegtsarenko55@gmail.com
Ucrânia, Kropivnitskii, 25006
A. Tkachuk
Vinnichenko Central Ukrainian State Pedagogical University
Email: olegtsarenko55@gmail.com
Ucrânia, Kropivnitskii, 25006
S. Ryabets
Vinnichenko Central Ukrainian State Pedagogical University
Email: olegtsarenko55@gmail.com
Ucrânia, Kropivnitskii, 25006
Arquivos suplementares