Nucleation of cracks near the free surface in deformed metallic nanomaterials with a bimodal structure

Resumo

A theoretical model that effectively describes the nucleation of cracks in stress fields of dislocation pile-ups near the free surface in metallic nanomaterials with a bimodal structure has been developed. The dependences of the critical shear stress τ_c (for the formation of a crack with an equilibrium length of 10 nm on a dislocation pile-up near the surface) on the size d of a grain containing the dislocation pile-up have been calculated for copper with a bimodal structure. Theoretically, it has been found that the critical shear stress τ_c for the nucleation of a crack near the free surface in a nanomaterial with a bimodal structure is approximately 30% higher than that for the crack nucleation within the nanomaterial at a distance from the free surface.