Magnetic Properties of Fullerene–Thermally Exfoliated Graphite Composites Doped with Sodium

Resumo

The magnetic properties (field range H = 0–50 kOe, temperature range T = 3–300 K), and structural features of a sodium-doped carbon composite material based on fullerene C₆₀ and thermally exfoliated graphite (TEG) are studied. The material is obtained with different ratios of the components by sintering at a pressure of 7 GPa and T = 600°C, at which it is found that significant amorphization of the crystal lattice of the initial C₆₀ occurs. The dia-, para-, and ferromagnetic components (M_D, M_PM, and M_FM) were separated from the total magnetic moment of the samples under study. It is found that a sodium dopant has no effect on the magnetic properties of the composite. Analysis of the M_PM(H) field dependences by using the Brillouin function for the fullerene-containing sample (i.e., without TEG) makes it possible to determine the quantum number of the total angular momentum of paramagnetic (PM) centers. Its value is found to be J = 1, which corresponds to elementary magnetic moment μ_PM = 2μ_B of a PM center. The concentration of PM centers is estimated at the level of N_PM ≈ (2–5) × 10¹⁸ g^–1 for most samples, including the material without TEG. The introduction of TEG into the initial composition and an increase in its proportion in the composite leads to a strong increase in the magnetic moment, which is explained by an increase in both the J value and the concentration of PM centers.