Influence of oxidized interlayers on magnetic properties of multilayer films based on amorphous ferromagnet–dielectric nanocomposites

Аннотация

Films of composites (Co₄₅Fe₄₅Zr₁₀)_x(Al₂O₃)_100–x, (Co₈₄Nb₁₄Ta₂)_x(SiO₂)_100–x, (Co₄₁Fe₃₉B₂₀)_x(SiO₂)_100–x and multilayer heterogeneous composite–composite structures {[(Co₄₅Fe₄₅Zr₁₀)_x(Al₂O₃)_100–x]/[(Co₄₅Fe₄₅Zr₁₀)_x(Al₂O₃)_100–x + N₂]}_n, {[(Co₄₅Fe₄₅Zr₁₀)_x(Al₂O₃)_100–x]/[(Co₄₅Fe₄₅Zr₁₀)_x(Al₂O₃)_100–x + O₂]}_n, {[(Co₄₁Fe₃₉B₂₀)_x(SiO₂)_100–x]/[(Co₄₁Fe₃₉B₂₀)_x(SiO₂)_100–x + O₂]}_n, and {[(Co₈₄Nb₁₄Ta₂)_x(SiO₂)_100–x]/[(Co₈₄Nb₁₄Ta₂)_x(SiO₂)_100–x + O₂]}_n have been deposited using the ionbeam sputtering method with a cyclic supply of reaction gases during deposition. The structure and magnetic properties of the films have been studied. It has been shown that the introduction of an oxidized interlayer makes it possible to suppress the perpendicular magnetic anisotropy in the (Co₄₅Fe₄₅Zr₁₀)_x(Al₂O₃)_100–x composite with the metallic phase concentration higher than the percolation threshold.