Estimation of thermodynamic properties of Cu–La binary alloy with modified Miedema’s theory


如何引用文章

全文:

开放存取 开放存取
受限制的访问 ##reader.subscriptionAccessGranted##
受限制的访问 订阅存取

详细

According to modified Miedema’s theory, mixing enthalpies (ΔH), excess entropies (SE), excess Gibbs free energy (GE), and component activities (a) of Cu–La binary alloy were estimated using the basic thermodynamic principles and some simple physical parameters of Cu and La, such as electronegativity, atomic volume and electron density. Based on the Cu–La binary alloy phase diagram, the Gibbs free energy of the phase precipitation reactions of Cu6La and Cu5La was deduced. The results showed that the values of ΔH, SE, and GE of Cu–La binary alloy were all negative. Compared to the ideal solution, the activities of the components presented a large negative deviation from Raoult’s law, which indicated that there was a strong interaction between Cu and La. The calculated data are well consistent with the experimental data. The Gibbs free energies of the phase precipitation reactions of Cu6La are lower than those for Cu5La, which means that Cu6La is thermodynamically more stable than Cu5La. Furthermore, the experimental results show that rareearth rich Cu6La phase particles in copper matrix are formed after La microalloying.

作者简介

Hai-hong Li

School of Environment and Materials Engineering; Institute of Metal Research

Email: shzhang@imr.ac.cn
中国, Yantai, 264005; Shenyang, 110016

Shi-hong Zhang

Institute of Metal Research

编辑信件的主要联系方式.
Email: shzhang@imr.ac.cn
中国, Shenyang, 110016

Yan Chen

Institute of Metal Research

Email: shzhang@imr.ac.cn
中国, Shenyang, 110016

Ming Cheng

Institute of Metal Research

Email: shzhang@imr.ac.cn
中国, Shenyang, 110016

Hong-wu Song

Institute of Metal Research

Email: shzhang@imr.ac.cn
中国, Shenyang, 110016

Jin-song Liu

Institute of Metal Research

Email: shzhang@imr.ac.cn
中国, Shenyang, 110016

补充文件

附件文件
动作
1. JATS XML

版权所有 © Pleiades Publishing, Ltd., 2016