Synthesis and properties of γ-Ga2O3–Al2O3 solid solutions

详细

The textural and structural properties of mixed oxides Ga₂O₃–Al₂O₃, obtained via impregnating γ-Al₂O₃ with a solution of Ga(NO₃)₃ and subsequent heat treatment, are studied. According to the results from X-ray powder diffraction, gallium ions are incorporated into the structure of aluminum oxide to form a solid solution of spinel-type γ-Ga₂O₃–Al₂O₃ up to a Ga₂O₃ content of 50 wt % of the total weight of the sample, accompanied by a reduction in the specific surface area, volume, and average pore diameter. It is concluded that when the Ga₂O₃ content exceeds 50 wt %, the β-Ga₂O₃ phase is observed along with γ-Ga₂O₃–Al₂O₃ solid solution. ⁷¹Ga and ²⁷Al NMR spectroscopy shows that gallium replaces aluminum atoms from the tetrahedral position to the octahedral coordination in the structure of γ-Ga₂O₃–Al₂O₃.