Mesoporous MgO: Synthesis, physico-chemical, and catalytic properties
- 作者: Maerle A.A.1, Kasyanov I.A.1, Moskovskaya I.F.1, Romanovsky B.V.1
-
隶属关系:
- Department of Chemistry
- 期: 卷 90, 编号 6 (2016)
- 页面: 1212-1216
- 栏目: Physical Chemistry of Nanoclusters and Nanomaterials
- URL: https://bakhtiniada.ru/0036-0244/article/view/168331
- DOI: https://doi.org/10.1134/S0036024416060108
- ID: 168331
如何引用文章
详细
Mesoporous MgO was obtained via the hydrothermal synthesis using both ionogenic and non-ionogenic surfactants as structure-directing templates. The materials prepared were characterized by SEM, BET-N2, XRD, and TG-DTA techniques. MgO particles are spherical 20-μm aggregates of primary oxide particles well shaped as rectangular parallelepipeds. Magnesium oxide samples have the specific surface area of 290–400 m2/g and pore sizes of 3.3–4.1 nm. Their mesoporous structure remained unchanged after calcination up to 350°C. Catalytic activity of mesoporous MgO was studied in acetone condensation reaction.
作者简介
A. Maerle
Department of Chemistry
Email: IFMoskovskaya@phys.chem.msu.ru
俄罗斯联邦, Moscow, 119991
I. Kasyanov
Department of Chemistry
Email: IFMoskovskaya@phys.chem.msu.ru
俄罗斯联邦, Moscow, 119991
I. Moskovskaya
Department of Chemistry
编辑信件的主要联系方式.
Email: IFMoskovskaya@phys.chem.msu.ru
俄罗斯联邦, Moscow, 119991
B. Romanovsky
Department of Chemistry
Email: IFMoskovskaya@phys.chem.msu.ru
俄罗斯联邦, Moscow, 119991
补充文件