Evolution of the Structural-Phase State of a Ti–Al– V–Mo Alloy During Severe Plastic Deformation and SubSequent Annealing


Citar

Texto integral

Acesso aberto Acesso aberto
Acesso é fechado Acesso está concedido
Acesso é fechado Somente assinantes

Resumo

The effect of the initial phase composition of a Ti–Al–V–Mo alloy (VT16 according to Russian classification) on the evolution of its structural-phase state during the formation of ultrafine-grained structure and subsequent annealing is investigated by methods of optical and transmission electron microscopy and x-ray diffraction analysis. The structure is produced by cyclic pressing with a change of the deformation axis in each cycle combined with a gradual decrease of the pressing temperature from 1073 to 723 K. As this takes place, α″ → α + β and β → α phase transitions are found to develop in the test alloy. The phase state of the ultrafinegrained material thus produced depends for the most part on its elemental composition and severe plastic deformation regime. Annealing below the recrystallization temperature is shown to give rise to a β→α phase transition and alloying element redistribution. The foregoing processes allow for retaining a high level of the strength properties of the alloy.

Sobre autores

G. Grabovetskaya

Institute of Strength Physics and Materials Science of the Siberian Branch of the Russian Academy of Sciences

Autor responsável pela correspondência
Email: grabg@ispms.tsc.ru
Rússia, Tomsk

I. Ratochka

Institute of Strength Physics and Materials Science of the Siberian Branch of the Russian Academy of Sciences

Email: grabg@ispms.tsc.ru
Rússia, Tomsk

I. Mishin

Institute of Strength Physics and Materials Science of the Siberian Branch of the Russian Academy of Sciences

Email: grabg@ispms.tsc.ru
Rússia, Tomsk

O. Zabudchenko

Institute of Strength Physics and Materials Science of the Siberian Branch of the Russian Academy of Sciences

Email: grabg@ispms.tsc.ru
Rússia, Tomsk

O. Lykova

Institute of Strength Physics and Materials Science of the Siberian Branch of the Russian Academy of Sciences

Email: grabg@ispms.tsc.ru
Rússia, Tomsk

Arquivos suplementares

Arquivos suplementares
Ação
1. JATS XML

Declaração de direitos autorais © Springer Science+Business Media New York, 2016