Exchange Spring in a Heterostructure with Pd0.96Fe0.04 Low-Temperature Ferromagnet

Resumo

The exchange bias of the magnetic hysteresis loop and the exchange-spring effect have been observed in thin-film heterostructures comprising layers of Pd_0.96Fe_0.04 low-temperature ferromagnet, metallic cobalt, and cobalt monoxide (CoO) grown on single-crystalline sapphire by methods of magnetron sputtering and molecular beam epitaxy in an ultrahigh-vacuum system. It is established that the exchange anisotropy of Pd_0.96Fe_0.04 layer in Pd_0.96Fe_0.04/CoO/Co/Al₂O₃ thin-film heterostructure is absent and the exchange-spring effect in this system is not manifested. In the case of a Pd_0.96Fe_0.04/Co/CoO/Al₂O₃ structure, it is shown that, according to the results of magnetometric measurements, the inversion of the order of antiferromagnetic and ferromagnetic layers leads to pinning of the magnetic moment of Pd_0.96Fe_0.04 layer at the interface with cobalt and to realization of the exchange-spring effect. Additional evidence in favor of this interpretation was obtained using the micromagnetic modeling of magnetic hysteresis loops.