Negative magnetoresistance of (1–x)La0.7Sr0.3MnO3/x(GeO2, Li4P2O7) composite ceramics
- Autores: Kabirov Y.V.1, Gavrilyachenko V.G.1, Bogatin A.S.1, Lyanguzov N.V.1, Gavrilyachenko T.V.1, Medvedev B.S.1
-
Afiliações:
- Southern Federal University
- Edição: Volume 42, Nº 3 (2016)
- Páginas: 278-279
- Seção: Article
- URL: https://bakhtiniada.ru/1063-7850/article/view/197861
- DOI: https://doi.org/10.1134/S1063785016030214
- ID: 197861
Citar
Resumo
Ceramics of (1–x)La0.7Sr0.3MnO3/x(GeO2) and (1–x)La0.7Sr0.3MnO3/x(Li4P2O7) compositions with x = 0.1–0.3 have been synthesized that possess high absolute values of isotropic negative magnetoresistance MR at room temperature. In a composite containing 20 mass % GeO2 as the barrier component, the negative magnetoresistance reaches MR = 15% in a magnetic field of 18 kOe, while an analogous composite with Li4P2O7 under identical conditions has MR = 16%.
Sobre autores
Yu. Kabirov
Southern Federal University
Autor responsável pela correspondência
Email: salv62@mail.ru
Rússia, Rostov-on-Don, 344006
V. Gavrilyachenko
Southern Federal University
Email: salv62@mail.ru
Rússia, Rostov-on-Don, 344006
A. Bogatin
Southern Federal University
Email: salv62@mail.ru
Rússia, Rostov-on-Don, 344006
N. Lyanguzov
Southern Federal University
Email: salv62@mail.ru
Rússia, Rostov-on-Don, 344006
T. Gavrilyachenko
Southern Federal University
Email: salv62@mail.ru
Rússia, Rostov-on-Don, 344006
B. Medvedev
Southern Federal University
Email: salv62@mail.ru
Rússia, Rostov-on-Don, 344006
Arquivos suplementares