电邮这篇文章 Formation of Nanosized Surface Layers of 03Kh17N12M2 Stainless Steel by Implantation of N+ Ions
- 作者: Vorob’ev V.L.1, Bykov P.V.1, Bayankin V.Y.1, Gil’mutdinov F.Z.1
-
隶属关系:
- Physical Technical Institute, Ural Branch, Russian Academy of Sciences
- 期: 卷 64, 编号 8 (2019)
- 页面: 1178-1183
- 栏目: Physics of Nanostructures
- URL: https://bakhtiniada.ru/1063-7842/article/view/203984
- DOI: https://doi.org/10.1134/S1063784219080231
- ID: 203984
如何引用文章
开放存取
##reader.subscriptionAccessGranted##
订阅存取
详细
Accumulation of nitrogen in nanosized surface layers of 03Kh17N12M2 stainless steel has been detected upon N+ ion implantation up to 14 at % together with metal nitrides, mainly of chromium nitride CrN and interstitial solid solution. It has been demonstrated that N+ ion implantation accompanied by preliminary irradiation by Ar+ and O+ ions decreases maximum nitrogen concentration by at least two times. It is assumed that this is stipulated by segregation to surface layers of iron atoms upon irradiation by Ar+ ions as well as formation of chromium oxide Cr2O3 and chromium hydroxide CrOOH upon irradiation by O+ ions.
作者简介
V. Vorob’ev
Physical Technical Institute, Ural Branch, Russian Academy of Sciences
编辑信件的主要联系方式.
Email: Vasily_L.84@mail.ru
俄罗斯联邦, Izhevsk, 426000
P. Bykov
Physical Technical Institute, Ural Branch, Russian Academy of Sciences
Email: Vasily_L.84@mail.ru
俄罗斯联邦, Izhevsk, 426000
V. Bayankin
Physical Technical Institute, Ural Branch, Russian Academy of Sciences
Email: Vasily_L.84@mail.ru
俄罗斯联邦, Izhevsk, 426000
F. Gil’mutdinov
Physical Technical Institute, Ural Branch, Russian Academy of Sciences
Email: Vasily_L.84@mail.ru
俄罗斯联邦, Izhevsk, 426000
补充文件