Study of volume and surface properties of the iron melts containing phosphorus impurity

封面

如何引用文章

全文:

开放存取 开放存取
受限制的访问 ##reader.subscriptionAccessGranted##
受限制的访问 订阅存取

详细

The structure-sensitive properties (density and surface tension) of iron melts were studied depending on the phosphorus impurity content at different temperatures. In the region of low phosphorus contents (hundredths of a percent), a compression effect and the appearance of negative deviations from Raoult’s law were detected. In the region of the higher compositions (tenths of a percent of phosphorus), a shift towards positive deviations is observed. The adsorption factor has a significant influence on the properties of the melt due to the formation of oxide film from the residual oxygen amount, its complete or partial disintegration at heating temperature. With increasing phosphorus content, the amount of adsorbed substance increased.

作者简介

K. Filippov

A.A. Baikov Institute of Metallurgy and Materials Science, Russian Academy of Sciences

Email: ksfilipp45@gmail.com

S. Anuchkin

A.A. Baikov Institute of Metallurgy and Materials Science, Russian Academy of Sciences

A. Aleksandrov

A.A. Baikov Institute of Metallurgy and Materials Science, Russian Academy of Sciences

参考

  1. Шахпазов, Е.Х. Физико-химические принципы восстановительного рафинирования высоколегированных сталей и ферросплавов от фосфора, сурьмы и других вредных примесей / Е.Х. Шахпазов, А.И. Зайцев, Б.М. Могутнов // Проблемы черной металлургии и материаловедения. 2010. №2. С.5—15. — (Shahpazov, E.H. Fiziko-himicheskie principy vosstanovitel'nogo rafinirovaniya vysokolegirovannyh staley i ferrosplavov ot fosfora, sur'my i drugih vrednyh primesey / E.H. Shahpazov, A.I. Zaytsev, B.M. Mogutnov // Problemy chernoy metallurgii i materialovedeniya. 2010. №2. P.5—15)
  2. Лякишев, Н.П. Некоторые фундаментальные проблемы металлургических процессов / Н.П. Лякишев // Сталь. 1991. №11. С.1—7. — (Lyakishev, N.P. Nekotorye fundamental'nye problemy metallurgicheskih protsessov / N.P. Lyakishev // Stal'. 1991. №11. P.1—7)
  3. Карасёв, В.П. Проведение дефосфорации при индукционной плавке стали / В.П. Карасёв, П.В. Ковалёв, С.В. Рябошук // Электрометаллургия. 2020. №6. С.2—7. — (Karasyov, V.P. Provedenie defosforatsii pri induktsionnoy plavke stali / V.P. Karasyov, P.V. Kovalyov, S.V. Ryaboshuk // Elektrometallurgiya. 2020. №6. P.2—7.)
  4. Лякишев, Н.П. Современное состояние технологии внепечного рафинирования стали / Н.П. Лякишев, А.Г. Шалимов. — М. : ЭЛИЗ, 2001. 50 с. — (Lyakishev, N.P. Sovremennoe sostoyanie tekhnologii vnepechnogo rafinirovaniya stali / N.P. Lyakishev, A.G. Shalimov. — M. : ELIZ, 2001. 50 p.)
  5. Филиппов, С.И. Теория металлургических процессов / С.И. Филиппов. — М. : Металлургия, 1967. 279 с. — (Filippov, S.I. Teoriya metallurgicheskih protsessov / S.I. Filippov. — M. : Metallurgiya, 1967. 279 p.)
  6. Несмеянов, А.Н. Давление пара химических элементов / А.Н. Несмеянов. — М. : Изд-во АН СССР, 1961. 395 с. — (Nesmeyanov, A.N. Davlenie para himicheskih elementov / A.N. Nesmeyanov. — M. : Izd-vo AN SSSR, 1961. 395 p.)
  7. Бояршинов, В.А. Рафинирующие переплавы стали и сплавов в вакууме / В.А. Бояршинов, А.Г. Шалимов, А.И. Щербаков, И. Петрман, И. Неедлы. — М. : Металлургия, 1979. 304 с. — (Boyarshinov, V.A. Rafiniruyushchie pereplavy stali i splavov v vakuume / V.A. Boyarshinov, A.G. Shalimov, A.I. Shcherbakov, I. Petrman, I. Needly. — M. : Metallurgiya, 1979. 304 p.)
  8. Филиппов, К.С. Исследование объемных и поверхностных свойств расплавов никеля, содержащих примесь висмута по параметрам плотности и поверхностного натяжения / К.С. Филиппов // Металлы. 2017. №4. С.77—83. — (Filippov, K.S. Volume and surface properties of nickel melts containing bismuth impurity determined from the density and the surface tension / K.S. Filippov // Russian Metallurgy (Metally). 2017. №7. P.606—611.)
  9. Филиппов, К.С. Исследование объемных и поверхностных свойств расплавов никеля, содержащих примесь сурьмы / К.С. Филиппов // Металлы. 2018. №4. С.86–95. — (Filippov, K.S. Volume and surface properties of antimony-containing nickel melts / K.S. Filippov // Russian Metallurgy (Metally). 2018. №7. Р.677—684.)
  10. Гольдштейн, Я.Е. Модифицирование и микролегирование чугуна и стали / Я.Е. Гольдштейн, В.Г. Мизин. — М. : Металлургия, 1986. 272 с. — (Gol'dshteyn, Ya.E. Modifitsirovanie i mikrolegirovanie chuguna i stali / Ya.E. Gol'dshteyn, V.G. Mizin. — M. : Metallurgiya, 1986. 272 p.)
  11. Филиппов, Е.С. Строение, физика и химия металлургических процессов / Е.С. Филиппов. — М. : Металлургия, 1995. 303 с. — (Filippov, E.S. Stroenie, fizika i himiya metallurgicheskih protsessov / E.S. Filippov. — M. : Metallurgiya, 1995. 303 p.)
  12. Баум, Б.А. Металлические жидкости / Б.А. Баум. — М. : Наука, 1979. 120 с. — (Baum, B.A. Metallicheskie zhidkosti / B.A. Baum. — M. : Nauka, 1979. 120 p.)
  13. Анучкин, С.Н. Исследование поверхностных свойств расплавов на основе никеля методом большой капли. I. Поверхностное натяжение / С.Н. Анучкин, В.Т. Бурцев, М.В. Загуменников, В.В. Сидоров, В.Е. Ригин // Металлы. 2010. №1. С.15—20. — (Ahuchkin, S.N. Study of the surface properties of nickel-based melts by the constrained drop method. I. Surface tension / S.N. Ahuchkin, V.T. Burtsev, M.V. Zagumennikov, V.V. Sidorov, V.E. Rigin // Russian Metallurgy (Metally). 2010. №1. P.13—17.)
  14. Анучкин, С.Н. Исследование поверхностных свойств расплавов на основе никеля методом большой капли. II. Плотность / С.Н. Анучкин, В.Т. Бурцев, М.В. Загуменников, В.В. Сидоров, В.Е. Ригин // Металлы. 2010. №3. С.3—7. — (Anuchkin, S.N. Study of the surface properties of nickel-based melts by the sessile drop method. II. Density / S.N. Anuchkin, V.T. Burtsev, M.V. Zagumennikov, V.V. Sidorov, V.E. Rigin // Russian Metallurgy (Metally). 2010. №5. P.371—374.)
  15. Nogi, K. Surface tension of liquid Fe-(Cu, Sn, Cr) and Ni-(Cu, Sn) binary alloys / K. Nogi, W.B. Chung, A. McLean, W.A. Miller // Mater. Trans. JIM. 1991. V.32. №2. Р.164—168.
  16. Ниженко, В.И. Поверхностное натяжение жидких металлов и сплавов: справочник / В.И. Ниженко, Л.И. Флока. — М. : Металлургия, 1981. 208 с. — (Nizhenko, V.I. Poverhnostnoe natyazhenie zhidkih metallov i splavov: spravochnik / V.I. Nizhenko, L.I. Floka. — M. : Metallurgiya, 1981. 208 p.)
  17. Найдич, Ю.В. Метод «большой капли» для определения поверхностного натяжения и плотности расплавленных металлов при высоких температурах / Ю.В. Найдич, В.И. Еременко // ФММ. 1961. Т.11. №6. С.883—888. — (Naydich, Yu.V. Metod «bol'shoy kapli» dlya opredeleniya poverhnostnogo natyazheniya i plotnosti rasplavlennyh metallov pri vysokih temperaturah / Yu.V. Naydich, V.I. Eremenko // FMM. 1961. T.11. №6. P.883—888.)
  18. Филиппов, К.С. Изменения внутренней энергии расплава на основе никеля при температурном гистерезисе плотности и поверхностного натяжения / К.С. Филиппов, В.И. Кашин, Е.Б. Мельникова // Физико-химические основы металлургических процессов : сб. статей. Научные сообщения 10-й Всесоюзной конференции. — М. : Черметинформация, 1991. Ч.III. С.149—151. — (Filippov, K.S. Izmeneniya vnutrenney energii rasplava na osnove nikelya pri temperaturnom gisterezise plotnosti i poverhnostnogo natyazheniya / K.S. Filippov, V.I. Kashin, E.B. Mel'nikova // Fiziko-himicheskie osnovy metallurgicheskih protsessov : sb. statey. Nauchnye soobshcheniya 10-y Vsesoyuznoy konferentsii. — M. : Chermetinformatsiya, 1991. V.III. P.149—151.)

补充文件

附件文件
动作
1. JATS XML
下载

版权所有 © Russian Academy of Sciences, 2025

Согласие на обработку персональных данных с помощью сервиса «Яндекс.Метрика»

1. Я (далее – «Пользователь» или «Субъект персональных данных»), осуществляя использование сайта https://journals.rcsi.science/ (далее – «Сайт»), подтверждая свою полную дееспособность даю согласие на обработку персональных данных с использованием средств автоматизации Оператору - федеральному государственному бюджетному учреждению «Российский центр научной информации» (РЦНИ), далее – «Оператор», расположенному по адресу: 119991, г. Москва, Ленинский просп., д.32А, со следующими условиями.

2. Категории обрабатываемых данных: файлы «cookies» (куки-файлы). Файлы «cookie» – это небольшой текстовый файл, который веб-сервер может хранить в браузере Пользователя. Данные файлы веб-сервер загружает на устройство Пользователя при посещении им Сайта. При каждом следующем посещении Пользователем Сайта «cookie» файлы отправляются на Сайт Оператора. Данные файлы позволяют Сайту распознавать устройство Пользователя. Содержимое такого файла может как относиться, так и не относиться к персональным данным, в зависимости от того, содержит ли такой файл персональные данные или содержит обезличенные технические данные.

3. Цель обработки персональных данных: анализ пользовательской активности с помощью сервиса «Яндекс.Метрика».

4. Категории субъектов персональных данных: все Пользователи Сайта, которые дали согласие на обработку файлов «cookie».

5. Способы обработки: сбор, запись, систематизация, накопление, хранение, уточнение (обновление, изменение), извлечение, использование, передача (доступ, предоставление), блокирование, удаление, уничтожение персональных данных.

6. Срок обработки и хранения: до получения от Субъекта персональных данных требования о прекращении обработки/отзыва согласия.

7. Способ отзыва: заявление об отзыве в письменном виде путём его направления на адрес электронной почты Оператора: info@rcsi.science или путем письменного обращения по юридическому адресу: 119991, г. Москва, Ленинский просп., д.32А

8. Субъект персональных данных вправе запретить своему оборудованию прием этих данных или ограничить прием этих данных. При отказе от получения таких данных или при ограничении приема данных некоторые функции Сайта могут работать некорректно. Субъект персональных данных обязуется сам настроить свое оборудование таким способом, чтобы оно обеспечивало адекватный его желаниям режим работы и уровень защиты данных файлов «cookie», Оператор не предоставляет технологических и правовых консультаций на темы подобного характера.

9. Порядок уничтожения персональных данных при достижении цели их обработки или при наступлении иных законных оснований определяется Оператором в соответствии с законодательством Российской Федерации.

10. Я согласен/согласна квалифицировать в качестве своей простой электронной подписи под настоящим Согласием и под Политикой обработки персональных данных выполнение мною следующего действия на сайте: https://journals.rcsi.science/ нажатие мною на интерфейсе с текстом: «Сайт использует сервис «Яндекс.Метрика» (который использует файлы «cookie») на элемент с текстом «Принять и продолжить».