Synthesis of Li1.3Al0.3Ti1.7(PO4)3 solid electrolyte from oxalate precursor

封面

如何引用文章

全文:

开放存取 开放存取
受限制的访问 ##reader.subscriptionAccessGranted##
受限制的访问 订阅存取

详细

A new efficient method of synthesis of solid electrolyte with high lithium-ion conductivity with NASICON structure of Li1.3Al0.3Ti1.7(PO4)3 (LATP) composition is proposed. The advantage of the developed method is the use of liquid-phase precursor based on titanium oxalate complex. It was found that at 750°C a single phase well crystallized LATP is formed. The total ionic conductivity value of LATP after sintering at 900°C measured by impedance spectroscopy was 2.6 × 10−4 S/cm at room temperature and the activation energy of conductivity was 0.28 eV. The presented synthesis method is promising for scale-up and mass production.

作者简介

G. Kunshina

Tananaev Institute of Chemistry - Subdivision of the Federal Research Centre “Kola Science Centre of the Russian Academy of Sciences”

Email: g.kunshina@ksc.ru
Apatity, 184209 Russia

I. Bocharova

Tananaev Institute of Chemistry - Subdivision of the Federal Research Centre “Kola Science Centre of the Russian Academy of Sciences”

编辑信件的主要联系方式.
Email: g.kunshina@ksc.ru
Apatity, 184209 Russia

参考

  1. Воропаева Д.Ю., Стенина И.А., Ярославцев А.Б. // Успехи химии. 2024. Т. 93 (6). С. RCR5126. https://doi.org/10.59761/RCR5126
  2. Yin J.-H., Zhu H., Yu S.-J. et al. // Adv. Eng. Mater. 2023. V. 25. P. 2300566. https://doi.org/10.1002/adem.202300566
  3. Stenina I., Novikova S., Voropaeva D. et al. // Batteries. 2023. V. 9. P. 407. https://doi.org/10.3390/batteries9080407
  4. Jian Z., Hu Y.-S., Ji X. et al. // Adv. Mater. 2017. V. 29. P. 1601925. https://doi.org/10.1002/adma.201601925
  5. Стенина И.А., Таранченко Е.О., Ильин А.Б. и др. // Журн. неорган. химии. 2023. T. 68. № 12. С. 1683. https://doi.org/10.31857/S0044457X23601360
  6. Lu X., Meng F., Huang S. et al. // Materials Letters. 2018. V. 230. P. 177. https://doi.org/10.1016/j.matlet.2018.07.103
  7. Wang S., Ben L., Li H. et al. // Solid State Ionics. 2014. V. 268. Part A. P. 110. https://doi.org/10.1016/j.ssi.2014.10.004
  8. Davis C. III, Nino J.C. // J. Am. Ceram. Soc. 2015. V. 98. P. 2422. https://doi.org/10.1111/jace.13638
  9. Wu P., Zhou W., Su X. et al. // Adv. Energy Mater. 2023. V. 13. P. 2203440. https://doi.org/10.1002/aenm.202203440
  10. Zhao E., Ma F., Jin Y. et al. // J. Alloys Compd. 2016. V. 680. P. 646. https://doi.org/10.1016/j.jallcom.2016.04.173
  11. Duluard S., Paillassa A., Puech L. et al. // J. Eur. Ceram. Soc. 2013. V. 33. P. 1145. https://doi.org/10.1016/j.jeurceramsoc.2012.08.005
  12. Schroeder M., Glatthaar S., Binder J.R. // Solid State Ionics. 2011. V. 201. P. 49. https://doi.org/10.1016/j.ssi.2011.08.014
  13. Kotobuki M., Koishi M. // J. Asian Ceram. Soc. 2020. V. 8(3). P. 891. https://doi.org/10.1080/21870764.2020.1793876
  14. Kotobuki M., Koishi M. // Ceram. Int. 2013. V. 39. № 4. P. 4645. https://doi.org/10.1016/j.ceramint.2012.10.206
  15. Куншина Г.Б., Громов О.Г., Локшин Э.П. и др. // Неорган. материалы. 2013. Т. 49. С. 59. https://doi.org/10.7868/S0002337X13010053
  16. Bharathi P., Wang S.-F. // ACS Applied Nano Materials. 2024. V. 7 (2). P. 1615. https://doi.org/10.1021/acsanm.3c04581
  17. Куншина Г.Б., Громов О.Г., Локшин Э.П. и др. // Журн. неорган. химии. 2014. Т. 59. С. 589. https://doi.org/10.7868/S0044457X14050122
  18. Zhao E., Ma F., Jin Y. et al. // J. Alloys Compd. 2016. V. 680. P. 646. https://doi.org/10.1016/j.jallcom.2016.04.173
  19. Yu S., Mertens A., Gao X. et al. // Funct. Mater. Lett. 2016. V. 9. P. 1650066. https://doi.org/10.1142/S1793604716500661
  20. Aono H., Sugimoto E., Sadaoka Y. et al. // J. Electrochem. Soc. 1990. V. 137. P. 1023. https://doi.org/10.1149/1.2086597
  21. Zaki A.A., Hashem H.M., Soltan S. et al. // Intern. J. Current Research. 2016. V. 8. P. 28385.
  22. Cretin M., Fabry P. // J. Eur. Ceram. Soc. 1999. V. 19. P. 2931.
  23. Куншина Г.Б., Бочарова И.В., Иваненко В.И. // Журн. прикл. химии. 2017. Т. 90. С. 312.
  24. Rossbach A., Neitzel-Grieshammer S. // Open Ceramics. 2022. V. 9. P. 100231. https://doi.org/10.1016/j.oceram.2022.100231
  25. Akhmetov N., Ovsyannikov N., Gvozdik N. et al. // J. Membrane Science. 2022. V. 643. P. 120002. https://doi.org/10.1016/j.memsci.2021.120002
  26. Yin J., Zhang H., Zeng Z. et al. // J. Alloys and Compd. 2024. V. 988. P. 174346. https://doi.org/10.1016/j.jallcom.2024.174346
  27. Bai F., Shang X., Nemori H. et al. // Solid State Ionics. 2019. V. 329. P. 40. https://doi.org/10.1016/j.ssi.2018.11.005
  28. Lu X., Wang R., Zhang F. et al. // Solid State Ionics. 2020. V. 354. P. 115417. https://doi.org/10.1016/j.ssi.2020.115417
  29. Dias J.A., Santagneli S.H., Messaddeq Y. // J. Phys. Chem. C. 2020. V. 124 (49). P. 26518. https://dx.doi.org/10.1021/acs.jpcc.0c07385
  30. Tolganbek N., Yerkinbekova Y., Khairullin A. et al. // Ceram. Int. 2021. V. 47. P. 18188. https://doi.org/10.1016/j.ceramint.2021.03.137
  31. Ren Y., Deng H., Zhao H. et al. // Ionics. 2020. V. 26. P. 6049. https://doi.org/10.1007/s11581-020-03781-5
  32. Han F., Westover A.S., Yue J. et al. // Nature Energy. 2019. V. 4. P. 187. https://doi.org/10.1038/s41560-018-0312-z
  33. Huang Y., Jiang Y., Zhou Y. et al. // Chem. Electro. Chem. 2019. V. 6. P. 6016. https://doi.org/10.1002/celc.201901687
  34. Tsai Y.C., Ku M.C., Hsieh C.T. et al. // J. Solid State Electro. Chem. 2024. V. 28. P. 2047. https://doi.org/10.1007/s10008-023-05729-x

补充文件

附件文件
动作
1. JATS XML
下载

版权所有 © Russian Academy of Sciences, 2025

Согласие на обработку персональных данных с помощью сервиса «Яндекс.Метрика»

1. Я (далее – «Пользователь» или «Субъект персональных данных»), осуществляя использование сайта https://journals.rcsi.science/ (далее – «Сайт»), подтверждая свою полную дееспособность даю согласие на обработку персональных данных с использованием средств автоматизации Оператору - федеральному государственному бюджетному учреждению «Российский центр научной информации» (РЦНИ), далее – «Оператор», расположенному по адресу: 119991, г. Москва, Ленинский просп., д.32А, со следующими условиями.

2. Категории обрабатываемых данных: файлы «cookies» (куки-файлы). Файлы «cookie» – это небольшой текстовый файл, который веб-сервер может хранить в браузере Пользователя. Данные файлы веб-сервер загружает на устройство Пользователя при посещении им Сайта. При каждом следующем посещении Пользователем Сайта «cookie» файлы отправляются на Сайт Оператора. Данные файлы позволяют Сайту распознавать устройство Пользователя. Содержимое такого файла может как относиться, так и не относиться к персональным данным, в зависимости от того, содержит ли такой файл персональные данные или содержит обезличенные технические данные.

3. Цель обработки персональных данных: анализ пользовательской активности с помощью сервиса «Яндекс.Метрика».

4. Категории субъектов персональных данных: все Пользователи Сайта, которые дали согласие на обработку файлов «cookie».

5. Способы обработки: сбор, запись, систематизация, накопление, хранение, уточнение (обновление, изменение), извлечение, использование, передача (доступ, предоставление), блокирование, удаление, уничтожение персональных данных.

6. Срок обработки и хранения: до получения от Субъекта персональных данных требования о прекращении обработки/отзыва согласия.

7. Способ отзыва: заявление об отзыве в письменном виде путём его направления на адрес электронной почты Оператора: info@rcsi.science или путем письменного обращения по юридическому адресу: 119991, г. Москва, Ленинский просп., д.32А

8. Субъект персональных данных вправе запретить своему оборудованию прием этих данных или ограничить прием этих данных. При отказе от получения таких данных или при ограничении приема данных некоторые функции Сайта могут работать некорректно. Субъект персональных данных обязуется сам настроить свое оборудование таким способом, чтобы оно обеспечивало адекватный его желаниям режим работы и уровень защиты данных файлов «cookie», Оператор не предоставляет технологических и правовых консультаций на темы подобного характера.

9. Порядок уничтожения персональных данных при достижении цели их обработки или при наступлении иных законных оснований определяется Оператором в соответствии с законодательством Российской Федерации.

10. Я согласен/согласна квалифицировать в качестве своей простой электронной подписи под настоящим Согласием и под Политикой обработки персональных данных выполнение мною следующего действия на сайте: https://journals.rcsi.science/ нажатие мною на интерфейсе с текстом: «Сайт использует сервис «Яндекс.Метрика» (который использует файлы «cookie») на элемент с текстом «Принять и продолжить».