Growth and spectral properties of Tm:BaY2F8 crystals with different Tm3+ concentration

详细

Tm³⁺:BaY₂F₈ (Tm:BYF) laser crystals with different doping concentrations were successfully grown by Czochralski method. The optimal growth parameters obtained are as follows: the pulling rate is 0.5 mm/h; the rotation speed is 5 rpm; the cooling rate is 10°C/h. Phase composition, absorption spectra, and fluorescence properties of crystals were studied by XRD and spectral methods. XRD analysis indicates that the crystal belongs to monoclinic system with the C2/m space group. The lattice parameters were calculated and the anisotropy of the crystals was studied, confirming that the a axis is the best growth direction. The absorption peaks around 790 nm became larger with increase of Tm³⁺ concentration. The cross section of 15% Tm:BYF crystal around 791 nm is 9.47 × 10^–21 cm². The 10% Tm:BYF crystal has the strongest emission peak around 1879.6 nm with the FWHM of 79 nm and the emission cross-section of 2.13 × 10^–21 cm², which is favorable for the 1.88 μm laser output.