Synthesis of metal catalysts Ni–Cu/Al2O3 by solutions combustion synthesis using sucrose as a fuel

封面

如何引用文章

全文:

开放存取 开放存取
受限制的访问 ##reader.subscriptionAccessGranted##
受限制的访问 订阅存取

详细

The Ni–Cu/Al2O3 catalysts used for the synthesis of nanofibrous carbon were prepared by the solution combusion method using sucrose as a fuel. The effect of different sucrose contents on the composition and textural characteristics of the resulting catalysts was studied. Catalyst samples were tested in a quartz flow reactor at atmospheric pressure and a temperature of 550°C (reaction medium — methane) for 6 h. The effect of organic fuel content on the performance of the catalyst precursor in the synthesis of nanofibrous carbon was studied. The resulting catalyst was a powder with a specific surface area of up to 128 m2/g.

作者简介

P. Kurmashov

Novosibirsk State Technical University

编辑信件的主要联系方式.
Email: kurmaschov@gmail.com
630073 Novosibirsk, Russian Federation

T. Gudyma

Novosibirsk State Technical University

Email: gudymatan@mail.ru
630073 Novosibirsk, Russian Federation

V. Golovakhin

Novosibirsk State Technical University

Email: golovaxin-valera@mail.ru
630073 Novosibirsk, Russian Federation

A. Ukhina

Institute of Solid State Chemistry and Mechanochemistry SB RAS

Email: auhina181@gmail.com
630128 Novosibirsk, Russian Federation

E. Maximovskiy

Nikolaev Institute of Inorganic Chemistry SB RAS

Email: eugene@niic.nsc.ru
630090 Novosibirsk, Russian Federation

A. Ishchenko

Boreskov Institute of Catalysis SB RAS

Email: arcady.ishchenko@gmail.com
630090 Novosibirsk, Russian Federation

A. Bannov

Novosibirsk State Technical University

Email: bannov_a@mail.ru
630073 Novosibirsk, Russian Federation

参考

  1. Hadian M., Marrevee D.P.F., Buist K.A. et al. // Chem. Eng. Sci. 2022. V. 260. № 22. P. 117938. https://doi.org/10.1016/j.ces.2022.117938
  2. Xu M., Lopez-ruiz J.A., Kovarik L. et al. // Appl. Catal. A, Gen. 2021. V. 611. P. 117967. https://doi.org/10.1016/j.apcata.2020.117967
  3. Фурсиков П.В., Тарасов Б.П. // АЭЭ. 2004. № 10. С. 24.
  4. Лобяк Е.В. Структура и свойства углеродных и азотсодержащих углеродных нанотрубок, синтезированных каталитическим пиролизом с использованием полимолибдатов Co, Ni, Fe: Дис. … канд. хим. наук. Новосибирск.: ИНХ СО РАН, 2018. 138 с.
  5. Курмашов П.Б. Совершенствование процесса синтеза нановолокнистого углерода и водорода на катализаторах, приготовленных методом синтеза горением раствора: Дис. … канд. техн. наук. Томск: ТПУ, 2021. 170 с.
  6. Курмашов П.Б., Максименко В.В., Баннов А.Г., Кувшинов Г.Г. // ХТТ. 2013. Т. 14. № 10. С. 635.
  7. Almiron J., Alcazar H., Churata R. et al.// Mater. Res. Express. 2018. V. 5. P. 125010. https://doi.org/10.1088/2053-1591/aadeb2
  8. Гудыма Т.С., Крутский Ю.Л., Максимовский Е.А., и др. // Известия вузов. Порошковая металлургия и функциональные покрытия. 2023. Т. 17. № 2. С. 35. https://doi.org/10.17073/1997-308X-2023-2-35-45 [Powder Metallurgy аnd Functional Coatings. 2023. V. 17, № 2. P. 35. https://doi.org/10.17073/1997-308X-2023-2-35-45]
  9. Хабиров Р.Р., Черкасова Н.Ю., Гудыма Т.С. и др. // Известия вузов. Порошковая металлургия и функциональные покрытия. 2024. T. 18. № 2. С. 23. https://doi.org/10.17073/1997-308X-2024-2-23-34 [Powder Metallurgy аnd Functional Coatings. 2024. V. 18. № 2. P. 23. https://doi.org/10.17073/1997-308X-2024-2-23-34]
  10. Дик Д.В., Гудыма Т.С., Филиппов А.А., Фомин В.М., Крутский Ю.Л. // Прикладная механика и техническая физика. 2024. Т. 65. № 2. С. 81. https://doi.org/10.15372/PMTF202315362
  11. Cuervo M.R., Asedegbega-Nieto E. et al.// J. Chromatogr. A. 2008. V. 1188. № 2. P. 264. https://doi.org/10.1016/j.chroma.2008.02.061
  12. Kovalenko G.A., Kuznetsova E.V., Mogilnykh Y.I. et al. // Carbon. 2001. V. 39. № 7. Р. 1033. https://doi.org/10.1016/S0008-6223(00)00216-5
  13. Kovalenko G.A., Perminova L.V., Rudina N.A. et al. // Journal Mol. Catal. B. Enzym. 2012. V. 76. P. 116. https://doi.org/10.1016/j.molcatb.2011.11.015
  14. Yu Y., Xue S., Zhao C., Barnych B., Sun G. // Appl. Surf. Sci. 2022. V. 582. P. 152392. https://doi.org/10.1016/j.apsusc.2021.152392
  15. Advances R.S.C., Zhao Y., Wang X. et al. // RSC Advances. 2012. V. 2. № 27. P. 10195. https://doi.org/10.1039/c2ra21338a
  16. Naghash A.R., Xu Z., Etsell T.H. // Chem. Mater. 2005. V. 17. P. 815. https://doi.org/10.1021/cm048476v
  17. Nimse P., Lokhande R.S., Jaybhaye S. // Int. J. Creat. Res. Thoughts. 2023. V. 11. № 4. P. 39. https://doi.org/10.1729/Journal.34166
  18. Solovev E.A., Kuvshinov D.G., Chukanov I.S., Ermakov D.Y., Kuvshinov G.G. // Theor. Found. Chem. Eng. 2008. V. 42. № 5. P. 611. https://doi.org/10.1134/S0040579508050230
  19. Reshetenko T.V., Avdeeva L.B., Ismagilov Z.R., Chuvilin A.L., Ushakov V.A. // Appl. Catal. A-Gen. 2003. V. 247. P. 51. https://doi.org/10.1016/s0926-860x(03)00080-2
  20. Ferk G., Stergar J., Drofenik M. et al.// Mat. Let. 2014. V. 124. P. 39. https://doi.org/10.1016/j.matlet.2014.03.030
  21. Gulyaeva Y., Bykova M.A., Bulavchenko O. et al.// Nanomaterials. 2021. V. 11. № 8. P. 2017. https://doi.org/10.3390/nano11082017
  22. Gronchi P., Kaddouri A., Centola P., Del Rosso R. // J. Solgel Sci. Technol. 2003. V. 26. № 1–3. P. 843. https://doi.org/10.1023/A:1020755801366
  23. Shen Y., Lua A. // RSC Advances. 2014. V. 4. № 79. P. 42159. https://doi.org/10.1039/c4ra04379k
  24. Chesnokov V.V., Chichkan A.S. // Int. J. Hydrogen Energy. 2009. V. 34. № 7. P. 2979. https://doi.org/10.1016/j.ijhydene.2009.01.074
  25. Афинеевский А.В. Прозоров Д.А., Осадчая Т.Ю., Никитин К.А. Способ механохимического синтеза никелевого катализатора гидрирования. А. с. 2722298 РФ // Б.И. 2020. № 16. С. 1.
  26. Kurmashov P.B., Ukhina A.V., Manakhov A. et al. // Appl. Sci. V. 13. № 6. P. 3962. https://doi.org/10.3390/app13063962
  27. Kumar A., Cross A., Manukyan K. et al.// Chem. Eng. J. 2015. V. 278. P. 46. https://doi.org/10.1016/J.CEJ.2015.01.012
  28. Yao D., Yang H., Chen H., Williams P.T. // Appl. Catal. B Environ. 2018. V. 239. P. 565. https://doi.org/10.1016/j.apcatb.2018.07.075
  29. Kruissink E.C., Reijen L.L., Ross J.R.H. // Van. Chem. Soc. 1981. V. 77. P. 649. https://doi.org/10.1039/F19817700649
  30. Prakash A.S., Khadar A.M.A., Patil K.C., Hegde M.S. // J. Mater. Synth. Process. 2002. V. 10. № 3. P. 135. https://doi.org/10.1023/A:1021986613158
  31. Курмашов П.Б., Баннов А.Г., Попов М.В., Казакова А.А., Ухина А.В., Кувшинов Г.Г. // ЖПХ. 2018. Т. 91. № 11. С. 1649. https://doi.org/10.1134/S0044461818110166 [Russian Journal of Applied Chemistry. 2018. V. 91, № 11, P. 1874. https://doi.org/10.1134/S1070427218110198]
  32. Mukasyan A., Epstein P., Dinka P. // J. Mater. Synth. Process. 2007. V. 31. P. 1789. https://doi.org/10.1016/J.PROCI.2006.07.052
  33. Курмашов П.Б., Попов М.В., Бресте А.Е, Ухина А.В., Баннов А.Г. // Доклады Российской академии наук. Химия, науки о материалах. 2023. T. 511. № 1. C. 68. https://doi.org/10.31857/S2686953522600660
  34. Zhuravlev V.D., Bamburov V.G., Beketov A.R., Perelyaeva L.A., Baklanova I.V. // Ceram. Int. 2013. V. 39. P. 1379. https://doi.org/10.1016/J.CERAMINT.2012.07.078
  35. Tahmasebi K., Paydar M.H. // Mater. Chem. Phys. 2008. V. 109. P. 156. https://doi.org/10.1016/J.MATCHEMPHYS.2007.11.009
  36. Fan Z., Weng W., Zhou J., Gu D., Xiao W. // J. Energy Chem. 2021. V. 58. P. 415. https://doi.org/10.1016/j.jechem.2020.10.049
  37. Wang I.W., Dagle R., Khan T. et al.// Catal. Sci. Technol. 2021. V. 11. № 14. P. 4911. https://doi.org/10.1039/D1CY00287B
  38. Smirnov A.A., Khromova S.A., Bulavchenko O.A. et al. // Kinet. Catal. 2014. V. 55. P. 72. https://doi.org/10.1134/S0023158414010145
  39. Седакова В.А., Громова Е.С. // Вестник фармации. 2011. № 4. C. 17.
  40. Menezes B.R.C., Ferreira F.V., Silva B.C. et al. // J. Mater. Sci. 2018. V. 53. P. 14311. https://doi.org/10.1007/s10853-018-2627-3
  41. Баннов А.Г. Синтез и модификация нановолокнистых углеродных материалов и графитоподобных материалов функционального назначения: Дис. …докт. хим. наук. М.: РХТУ, 2022. 378 с.

补充文件

附件文件
动作
1. JATS XML
下载

版权所有 © Russian Academy of Sciences, 2025

Согласие на обработку персональных данных с помощью сервиса «Яндекс.Метрика»

1. Я (далее – «Пользователь» или «Субъект персональных данных»), осуществляя использование сайта https://journals.rcsi.science/ (далее – «Сайт»), подтверждая свою полную дееспособность даю согласие на обработку персональных данных с использованием средств автоматизации Оператору - федеральному государственному бюджетному учреждению «Российский центр научной информации» (РЦНИ), далее – «Оператор», расположенному по адресу: 119991, г. Москва, Ленинский просп., д.32А, со следующими условиями.

2. Категории обрабатываемых данных: файлы «cookies» (куки-файлы). Файлы «cookie» – это небольшой текстовый файл, который веб-сервер может хранить в браузере Пользователя. Данные файлы веб-сервер загружает на устройство Пользователя при посещении им Сайта. При каждом следующем посещении Пользователем Сайта «cookie» файлы отправляются на Сайт Оператора. Данные файлы позволяют Сайту распознавать устройство Пользователя. Содержимое такого файла может как относиться, так и не относиться к персональным данным, в зависимости от того, содержит ли такой файл персональные данные или содержит обезличенные технические данные.

3. Цель обработки персональных данных: анализ пользовательской активности с помощью сервиса «Яндекс.Метрика».

4. Категории субъектов персональных данных: все Пользователи Сайта, которые дали согласие на обработку файлов «cookie».

5. Способы обработки: сбор, запись, систематизация, накопление, хранение, уточнение (обновление, изменение), извлечение, использование, передача (доступ, предоставление), блокирование, удаление, уничтожение персональных данных.

6. Срок обработки и хранения: до получения от Субъекта персональных данных требования о прекращении обработки/отзыва согласия.

7. Способ отзыва: заявление об отзыве в письменном виде путём его направления на адрес электронной почты Оператора: info@rcsi.science или путем письменного обращения по юридическому адресу: 119991, г. Москва, Ленинский просп., д.32А

8. Субъект персональных данных вправе запретить своему оборудованию прием этих данных или ограничить прием этих данных. При отказе от получения таких данных или при ограничении приема данных некоторые функции Сайта могут работать некорректно. Субъект персональных данных обязуется сам настроить свое оборудование таким способом, чтобы оно обеспечивало адекватный его желаниям режим работы и уровень защиты данных файлов «cookie», Оператор не предоставляет технологических и правовых консультаций на темы подобного характера.

9. Порядок уничтожения персональных данных при достижении цели их обработки или при наступлении иных законных оснований определяется Оператором в соответствии с законодательством Российской Федерации.

10. Я согласен/согласна квалифицировать в качестве своей простой электронной подписи под настоящим Согласием и под Политикой обработки персональных данных выполнение мною следующего действия на сайте: https://journals.rcsi.science/ нажатие мною на интерфейсе с текстом: «Сайт использует сервис «Яндекс.Метрика» (который использует файлы «cookie») на элемент с текстом «Принять и продолжить».