Size Effect in Silver Oxidation By Nitrogen Dioxide
- Autores: Kalinkin A.V.1, Smirnov M.Y.1, Klembovskii I.O.2, Sorokin A.M.1, Gladky A.Y.1, Bukhtiyarov V.I.1,2
-
Afiliações:
- Boreskov Institute of Catalysis, Siberian Branch
- Novosibirsk State University
- Edição: Volume 59, Nº 7 (2018)
- Páginas: 1726-1729
- Seção: Article
- URL: https://bakhtiniada.ru/0022-4766/article/view/161785
- DOI: https://doi.org/10.1134/S0022476618070284
- ID: 161785
Citar
Resumo
X-ray photoelectron spectroscopy is applied to study at room temperature and pressure of 10–5 Torr the interaction of NO2 with a model sample obtained by thermal deposition of silver on the graphite surface. Scanning tunneling microscopy shows that in this case, silver particles with a size of D = 4–11 nm are formed on the surface. For comparison, polycrystalline silver foil is studied under similar conditions. It is found that such a treatment leads to silver oxidation in the Ag/C sample while the foil remains unchanged under these conditions.
Palavras-chave
Sobre autores
A. Kalinkin
Boreskov Institute of Catalysis, Siberian Branch
Autor responsável pela correspondência
Email: avkalinkin@mail.ru
Rússia, Novosibirsk
M. Smirnov
Boreskov Institute of Catalysis, Siberian Branch
Email: avkalinkin@mail.ru
Rússia, Novosibirsk
I. Klembovskii
Novosibirsk State University
Email: avkalinkin@mail.ru
Rússia, Novosibirsk
A. Sorokin
Boreskov Institute of Catalysis, Siberian Branch
Email: avkalinkin@mail.ru
Rússia, Novosibirsk
A. Gladky
Boreskov Institute of Catalysis, Siberian Branch
Email: avkalinkin@mail.ru
Rússia, Novosibirsk
V. Bukhtiyarov
Boreskov Institute of Catalysis, Siberian Branch; Novosibirsk State University
Email: avkalinkin@mail.ru
Rússia, Novosibirsk; Novosibirsk
Arquivos suplementares