Effects of annealing on elemental composition and quality of CZTSSe thin films obtained by spray pyrolysis
- Autores: Dermenji L.1, Curmei N.1, Guc M.2, Gurieva G.3, Rusu M.3,4, Fedorov V.4, Bruc L.1, Sherban D.1, Schorr S.3,5, Simashkevich A.1, Arushanov E.1
-
Afiliações:
- Institute of Applied Physics
- IREC, Catalonia Institute for Energy Research, Sant Adrià del Besòs
- Helmholtz-Zentrum Berlin für Materialien und Energie GmbH
- Moldova State University
- Institute of Geological Sciences
- Edição: Volume 52, Nº 6 (2016)
- Páginas: 509-514
- Seção: Article
- URL: https://bakhtiniada.ru/1068-3755/article/view/229938
- DOI: https://doi.org/10.3103/S1068375516060041
- ID: 229938
Citar
Resumo
The spray pyrolysis was used for the deposition of Cu2ZnSn(S, Se)4 (CZTSSe) kesterite thin films. The basic spray pyrolysis solution was prepared from two precursor solutions containing thiourea and cooled to a temperature near 1°C, which leads to minimizing the number of insoluble hydrates of copper chloride. The optimal substrate temperature was 350°C and the distance from the sprayer nozzle 30 cm. The as-deposited Cu2ZnSnS4 layers were annealed in S2 atmosphere for the compensation of the sulfur deficiency and with the addition of Sn in order to avoid tin loss. Cu2ZnSn(S, Se)4 thin films were obtained after the annealing of as-deposited films in the (S2 + Se2) atmosphere. The surface morphology and composition of obtained thin films were investigated using the energy dispersive X-ray (EDX) microanalysis and Raman spectroscopy measurements. The structural characterization by the grazing incidence X-ray diffraction (GIXRD) showed the presence of Cu2–xS phases in all of the annealed thin films. For the Se/(S + Se) ratio of the thin films annealed in the (S + Se) atmosphere was established from EDX measurements and analysis of GIXRD data, the results are in satisfactory agreement.
Sobre autores
L. Dermenji
Institute of Applied Physics
Email: leonid.bruc@phys.asm.md
Moldova, Chisinau, MD-2028
N. Curmei
Institute of Applied Physics
Email: leonid.bruc@phys.asm.md
Moldova, Chisinau, MD-2028
M. Guc
IREC, Catalonia Institute for Energy Research, Sant Adrià del Besòs
Email: leonid.bruc@phys.asm.md
Espanha, Barcelona, 08930
G. Gurieva
Helmholtz-Zentrum Berlin für Materialien und Energie GmbH
Email: leonid.bruc@phys.asm.md
Alemanha, Berlin, 14109
M. Rusu
Helmholtz-Zentrum Berlin für Materialien und Energie GmbH; Moldova State University
Email: leonid.bruc@phys.asm.md
Alemanha, Berlin, 14109; Chisinau, 2009
V. Fedorov
Moldova State University
Email: leonid.bruc@phys.asm.md
Moldova, Chisinau, 2009
L. Bruc
Institute of Applied Physics
Autor responsável pela correspondência
Email: leonid.bruc@phys.asm.md
Moldova, Chisinau, MD-2028
D. Sherban
Institute of Applied Physics
Email: leonid.bruc@phys.asm.md
Moldova, Chisinau, MD-2028
S. Schorr
Helmholtz-Zentrum Berlin für Materialien und Energie GmbH; Institute of Geological Sciences
Email: leonid.bruc@phys.asm.md
Alemanha, Berlin, 14109; Berlin, 12249
A. Simashkevich
Institute of Applied Physics
Email: leonid.bruc@phys.asm.md
Moldova, Chisinau, MD-2028
E. Arushanov
Institute of Applied Physics
Email: leonid.bruc@phys.asm.md
Moldova, Chisinau, MD-2028
Arquivos suplementares