Corrosion Performance of Nano-Alumina Coatings over Anodized Aluminum Alloy by Dip Coating Method


Дәйексөз келтіру

Толық мәтін

Ашық рұқсат Ашық рұқсат
Рұқсат жабық Рұқсат берілді
Рұқсат жабық Тек жазылушылар үшін

Аннотация

Alumina coatings are widely used to enhance the wear, abrasion, and corrosion resistance of metal components. This investigation aims at studying the alumina sol-gel coating on the anodized aluminum alloy surface using a dip coating technique. A stable alumina coating was deposited over the anodized aluminum surface using oxime-modified aluminum(III) isopropoxide as sol-gel precursor. The scanning electron microscopy image of the coated anodized sample suggests deposition of a uniform and crack-free aluminum coating. The corrosion resistances of bare, anodized, and coated anodized aluminum alloy samples were investigated by electrochemical impedance spectroscopy and potentiodynamic polarization in 3.5 wt % aqueous NaCl solution. An appreciable shifting was observed in the equilibrium corrosion potential (Ecorr) and the corrosion current density (icorr) values of both anodized and coated anodized samples: i.e. Ecorr: from –1377.11 mV (anodized) to –711.54 mV (coated anodized) and icorr: from 80.37 μA/cm2 (anodized) to 0.090 μA/cm2 (coated anodized). The results clearly indicate the corrosion resistive behavior of nano-alumina coatings.

Авторлар туралы

Dalip Singh

School of Automobile Mechanical and Mechatronics, Manipal University

Email: dhayal21v@gmail.com
Үндістан, Jaipur, 303007

Veena Dhayal

Department of Chemistry, Manipal University

Хат алмасуға жауапты Автор.
Email: dhayal21v@gmail.com
Үндістан, Jaipur, 303007

Dinesh Chandra Agarwal

National Institute for Research and Development in Defence Shipbuilding (NIRDESH)

Email: dhayal21v@gmail.com
Үндістан, New Delhi

Қосымша файлдар

Қосымша файлдар
Әрекет
1. JATS XML

© Allerton Press, Inc., 2019