Phase Transitions and Electrophysical Properties of Tungsten(VI) Oxide in a 83–673 K Temperature Range


Дәйексөз келтіру

Толық мәтін

Ашық рұқсат Ашық рұқсат
Рұқсат жабық Рұқсат берілді
Рұқсат жабық Тек жазылушылар үшін

Аннотация

The paper studies the changes in the crystal structure and dielectric properties of tungsten(VI) oxide (WO3) in the temperature range from 83 to 673 K. Investigations are performed using X-ray phase analysis and scanning electron microscopy of the material under study. It is found that the phase transition from triclinic to monoclinic structure occurs at 83 K for the tungsten(VI) oxide powder. When the powder is heated up to 673 K, its crystal structure again becomes triclinic. The peak intensity of the initial WO3 powder heated up to 673 K is observed at a Bragg angle of 24.34 degrees, while that of the cooled WO3 powder occurs at 23.08 degrees. The powder calcination changes the crystal lattice parameter at a Bragg angle of 24.34 degrees, such that а = 6.333 Å and а = 6.339 Å for the initial and calcined WO3 powder, respectively. The main electrophysical properties are obtained for the WO3 powder specimens, namely: surface resistance, specific surface resistance and conductivity, electric conductivity, permittivity, dissipation factor.

Авторлар туралы

N. Cherkashina

Belgorod State Technological University named after V. G. Shukhov

Хат алмасуға жауапты Автор.
Email: natalipv13@mail.ru
Ресей, Belgorod

V. Pavlenko

Belgorod State Technological University named after V. G. Shukhov

Email: natalipv13@mail.ru
Ресей, Belgorod

R. Yastrebinskii

Belgorod State Technological University named after V. G. Shukhov

Email: natalipv13@mail.ru
Ресей, Belgorod

Қосымша файлдар

Қосымша файлдар
Әрекет
1. JATS XML

© Springer Science+Business Media, LLC, part of Springer Nature, 2019