Structure and Properties of VT6 Alloy Obtained by Layered Selective Sintering of a Powder


Дәйексөз келтіру

Толық мәтін

Ашық рұқсат Ашық рұқсат
Рұқсат жабық Рұқсат берілді
Рұқсат жабық Тек жазылушылар үшін

Аннотация

This paper is focused on a clarification and analysis of the regularities of formation of the structure and properties of samples of the titanium-based alloy VT6, obtained by methods of conventional metallurgy and formed by layered selective electron-beam sintering in vacuum (using the Arcam A2X (3D printer) system (Arcam, Sweden)) of VT6 titanium powder with particle size 40–100 μm. Additional modification of the samples was realized by irradiating the surface with an intense pulsed electron beam (15 keV, 45 J/cm2, 200 μs, 10 pulses, 0.3 s–1, 3.5·10–2 Pa). It is shown that the action of a pulsed electron beam on the surface of samples formed by layered selective electron-beam sintering leads to a significant reduction in the porosity of the surface layer of the material and formation in the surface layer of a polycrystalline structure (grain size 15–60 μm) with a substructure in the form of crystallization cells (cell size 0.5–1.2 μm). Electron-beam processing of samples prepared by methods of conventional metallurgy for the indicated electron-beam parameters leads to the formation in the surface layer of a polycrystalline structure (grain size 50–800 μm) with a laminar intragrain substructure. Mechanical tests, performed by stretching flat samples, showed that the highest combination of mechanical strength and plasticity is possessed by samples obtained by layered selective electron-beam sintering with subsequent irradiation by an intense pulsed electron beam.

Авторлар туралы

A. Teresov

Institute of High-Current Electronics of the Siberian Branch of the Russian Academy of Sciences

Хат алмасуға жауапты Автор.
Email: tad514@yandex.ru
Ресей, Tomsk

Yu. Ivanov

Institute of High-Current Electronics of the Siberian Branch of the Russian Academy of Sciences; National Research Tomsk Polytechnic University

Email: tad514@yandex.ru
Ресей, Tomsk; Tomsk

E. Petrikova

Institute of High-Current Electronics of the Siberian Branch of the Russian Academy of Sciences

Email: tad514@yandex.ru
Ресей, Tomsk

N. Koval

Institute of High-Current Electronics of the Siberian Branch of the Russian Academy of Sciences

Email: tad514@yandex.ru
Ресей, Tomsk

Қосымша файлдар

Қосымша файлдар
Әрекет
1. JATS XML

© Springer Science+Business Media, LLC, part of Springer Nature, 2017