Отправить статью по E-mail The Effect of High-Temperature Annealing on the Structural-Phase State of Ultrafine Grain Steel 0.1C–2V–1Ti–Fe
- Авторы: Popova N.A.1,2, Nikonenko E.L.1,3, Sizorenko N.R.1, Koneva N.A.1
-
Учреждения:
- Tomsk State University of Architecture and Building
- Institute of Strength Physics and Materials Science of the Siberian Branch of the Russian Academy of Sciences
- National Research Tomsk Polytechnic University
- Выпуск: Том 60, № 4 (2017)
- Страницы: 615-623
- Раздел: Article
- URL: https://bakhtiniada.ru/1064-8887/article/view/238149
- DOI: https://doi.org/10.1007/s11182-017-1116-5
- ID: 238149
Цитировать
Открытый доступ
Доступ предоставлен
Только для подписчиков
Аннотация
Using transmission electron microscopy and X-ray diffraction analysis, the structural-phase state of steel 0.1C–2V–1Ti–Fe, deformed by the SPD methods and subjected to high-temperature annealing at the temperatures 600 and 700°С, is investigated. The influence of the steady temperature on the grain size, steel phase composition, carbide transformations, carbide particle size and distribution density, carbon distribution, and fine-structure parameters are determined. A special focus is made on the sources of internal stress.
Об авторах
N. Popova
Tomsk State University of Architecture and Building; Institute of Strength Physics and Materials Science of the Siberian Branch of the Russian Academy of Sciences
Автор, ответственный за переписку.
Email: natalya-popova-44@mail.ru
Россия, Tomsk; Tomsk
E. Nikonenko
Tomsk State University of Architecture and Building; National Research Tomsk Polytechnic University
Email: natalya-popova-44@mail.ru
Россия, Tomsk; Tomsk
N. Sizorenko
Tomsk State University of Architecture and Building
Email: natalya-popova-44@mail.ru
Россия, Tomsk
N. Koneva
Tomsk State University of Architecture and Building
Email: natalya-popova-44@mail.ru
Россия, Tomsk
Дополнительные файлы