Enviar artigo por via de e-mail Spark plasma sintering of β-SiAlON–BN composites from combustion-synthesized powders
- Autores: Nefedova E.V.1, Grigoryev E.G.1, Fokin D.A.1, Smirnov K.L.2
-
Afiliações:
- National Research Nuclear University MEPhI
- Institute of Structural Macrokinetics and Materials Science
- Edição: Volume 25, Nº 4 (2016)
- Páginas: 229-233
- Seção: Article
- URL: https://bakhtiniada.ru/1061-3862/article/view/195756
- DOI: https://doi.org/10.3103/S1061386216040075
- ID: 195756
Citar
Acesso aberto
Acesso está concedido
Somente assinantes
Resumo
Investigated was the spark plasma sintering (SPS) of β-SiAlON/0–30 wt % BN ceramic composites. The raw materials (β-Si5AlON7 and BN powders) were prepared by infiltration-mediated combustion synthesis (CS). Experimentally established were the following process parameters for SPS of composites with high relative density (>95%) and flexural strength of 250–300 MPa: (a) heating rate 50 deg/min, (b) maximum temperature 1650–1750°C, (c) and holding time 5 min.
Palavras-chave
Sobre autores
E. Nefedova
National Research Nuclear University MEPhI
Email: kosm@ism.ac.ru
Rússia, Moscow, 115409
E. Grigoryev
National Research Nuclear University MEPhI
Email: kosm@ism.ac.ru
Rússia, Moscow, 115409
D. Fokin
National Research Nuclear University MEPhI
Email: kosm@ism.ac.ru
Rússia, Moscow, 115409
K. Smirnov
Institute of Structural Macrokinetics and Materials Science
Autor responsável pela correspondência
Email: kosm@ism.ac.ru
Rússia, Chernogolovka, Moscow, 142432
Arquivos suplementares