SYNTHESIS, THERMAL AND ELECTRICAL PROPERTIES OF Bi2NiNb2O9 WITH PYROCHLORE STRUCTURE

封面

如何引用文章

全文:

开放存取 开放存取
受限制的访问 ##reader.subscriptionAccessGranted##
受限制的访问 订阅存取

详细

Nickel-containing cubic pyrochlore Bi2NiNb2O9 (sp. gr. Fd3m, a = 10.53657(6) Å) was synthesized by the citrate method. At the synthesis temperature of 1050°C, low-porosity ceramics with unclear grain boundary outlines are formed. The disordered structure of pyrochlore (sp. gr. Fd3m, a = 10.53784 Å, Z = 4) was refined by the Rietveld method based on X-ray powder diffraction data. The studied pyrochlore belongs to isotropically expanding oxide compounds with an average value of the thermal expansion coefficient of (6.4 × 10−6)°C−1 in the range of 30–750°C. Above 1110°C, thermal dissociation of Bi2NiNb2O9 occurs with the formation of the impurity phase NiNb2O6. Bi2NiNb2O9 is characterized by a high activation energy of 1.43 eV and a frequency- and temperature-independent permittivity of 144 (up to 300°C), low dielectric losses of ~ 0.002 at 1 MHz. The studied ceramics can be used as a high-frequency dielectric material in the creation of multilayer ceramic capacitors.

作者简介

K. Badanina

Syktyvkar State University

Email: Badanina-Ksenia@mail.ru
Syktyvkar, 167001 Russia

N. Sekushin

Institute of Chemistry of the Komi Science Center UB RAS

Email: Badanina-Ksenia@mail.ru
Syktyvkar, 167982 Russia

M. Krzhizhanovskaya

Saint Petersburg State University

Email: Badanina-Ksenia@mail.ru
St. Petersburg, 199034 Russia

N. Zhuk

Syktyvkar State University

编辑信件的主要联系方式.
Email: Badanina-Ksenia@mail.ru
Syktyvkar, 167001 Russia

参考

  1. Hiroi Z., Yamaura J.-I., Yonezawa S. et al. // Physica C. 2007. V. 460–462. P. 20. https://doi.org/10.1016/j.physc.2007.03.023
  2. Giampaoli G., Siritanon T., Day B. et al. // Prog. Solid State Chem. 2018. V. 50. P. 16. https://doi.org/10.1016/j.progsolidstchem.2018.06.001
  3. Pandey J., Shrivastava V., Nagarajan R. // Inorg. Chem. 2018. V. 57. № 21. P. 13667. https://doi.org/10.1021/acs.inorgchem.8b02258
  4. Yu S., Li L., Zheng H. // Alloys Compd. 2017. V. 699. P. 68. https://doi.org/10.1016/j.jallcom.2016.12.333
  5. Guo Q., Li L., Yu S. et al. // Ceram. Int. 2018. V. 44. № 1. P. 333. https://doi.org/10.1016/j.ceramint.2017.09.177
  6. Vanderah T.A., Siegrist T., Lufaso M.W. et al. // Eur. J. Inorg. Chem. 2006. V. 2006. № 23. P. 4908. https://doi.org/10.1002/ejic.200600661
  7. Miles G.C., West A.R. // J. Am. Ceram. Soc. 2006. V. 89. № 3. P. 1042. https://doi.org/10.1111/j.1551-2916.2005.00799.x
  8. Subramanian M.A., Aravanmadan G., Subba Rao G.V. // Prog. Solid State Chem. 1983. V. 15. № 2. P. 55. https://doi.org/10.1016/0079-6786(83)90001-8
  9. Zhuk N.A., Kryhizhanovskaya M.G., Koroleva A.V. et al. // Inorg. Chem. 2021. V. 60. № 7. P. 4924. https://doi.org/10.1021/acs.inorgchem.1e00007
  10. Zhuk N.A., Kryhizhanovskaya M.G., Sekushin N.A. et al. // J. Mater. Res. Technol. 2023. V. 22. P. 1791. https://doi.org/10.1016/j.jmrt.2022.12.059
  11. Vanderah T.A., Lufaso M.W., Adler A.U. et al. // J. Solid State Chem. 2006. V. 179. P. 3467. https://doi.org/10.1016/j.jssc.2006.07.014
  12. Zhuk N.A., Badannia K.A., Korolev R.I. et al. // Inorganics. 2023. V. 11. № 7. P. 288. https://doi.org/10.3390/inorganics11070288
  13. Valant M., Suvorov D. // J. Am. Ceram. Soc. 2005. V. 88. № 9. P. 2540. https://doi.org/10.1111/j.1551-2916.2005.00439.x
  14. Hassan A., Mustafa G.M., Abbas S.K. et al. // Ceram. Int. 2019. V. 45. № 12. P. 14576. https://doi.org/10.1016/j.ceramint.2019.04.175
  15. Tan P.Y., Tan K.B., Khaw C.C. et al. // Ceram. Int. 2014. V. 40. № 3. P. 4237. https://doi.org/10.1016/j.ceramint.2013.08.087
  16. Guo Q., Li L., Yu S. et al. // Ceram. Int. 2018. V. 44. № 1. P. 333. https://doi.org/10.1016/j.ceramint.2017.09.177
  17. Dasin N.A.M., Tan K.B., Khaw C.C. et al. // Mater. Chem. Phys. 2019. V. 242. P. 122558. https://doi.org/10.1016/j.matchemphys.2019.122558
  18. Abdullah A., Wan Khalid W.E.F., Abdullah S.Z. // Appl. Mechanics and Materials. 2015. V. 749. P. 30. https://doi.org/10.4028/www.scientific.net/AMM.749.30
  19. Bruker AXS. Topas 5.0. General profile and structure analysis software for powder diffraction data. Karlsruhe, Germany. 2014.
  20. Bubnova R.S., Firsova V.A., Filatov S.K. // Glass Phys. Chem. 2013. V. 39. № 3. P. 347. https://doi.org/10.1134/S108765961303005X
  21. Langreiter T., Kahlenberg V. // Crystals. 2015. V. 5. № 1. P. 143. https://doi.org/10.3390/cryst5010143
  22. Mansie T.J.S., Millington A., Dube P.A. et al. // J. Solid State Chem. 2016. V. 236. P. 19. https://doi.org/10.1016/j.jssc.2015.07.048
  23. Zhuk N.A., Kryhizhanovskaya M.G., Sekushin N.A. et al. // Ceram. Int. 2023. V. 49. № 2. P. 2934. https://doi.org/10.1016/j.ceramint.2022.09.278
  24. Zhuk N.A., Kryhizhanovskaya M.G., Sekushin N.A. et al. // ACS Omega. 2021. V. 6. № 36. P. 23262. https://doi.org/10.1021/acsomega.1c02969
  25. Shannon R.D. // Acta Crystallogr., Sect. A: Found. Crystallogr. 1976. V. 32. № 5. P. 751. https://doi.org/10.1107/S0567739476001551
  26. Koroleva M.S., Pitt I.V., Istomin E.I. // Chim. Techno Acta. 2017. V. 4. № 4. P. 231. https://doi.org/10.15826/chimtech/2017.4.4.04
  27. Nguyen H.B., Norén L., Liu Y. et al. // J. Solid State Chem. 2007. V. 180. № 9. P. 2558. https://doi.org/10.1016/j.jssc.2007.07.003
  28. Zhuk N.A., Kryhizhanovskaya M.G. // Ceram. Int. 2021. V. 47. № 21. P. 30099. https://doi.org/10.1016/j.ceramint.2021.07.187
  29. Alfred A.L., Rochow E.G. // J. Inorg. Nucl. Chem. 1958. V. 5. № 4. P. 264. https://doi.org/10.1016/0022-1902(58)80003-2
  30. Zhuk N.A., Kryhizhanovskaya M.G., Belyy V.A. et al. // Chem. Mater. 2020. V. 32. № 13. P. 5493. https://doi.org/10.1021/acs.chemmater.0c00010
  31. Kurty K.V.G., Rajagopalan S., Mathews C.K. et al. // Mater. Res. Bull. 1994. V. 29. № 7. P. 759. https://doi.org/10.1016/0025-5408(94)90201-1
  32. Shukla R., Vasundhara K., Krishna P.S.R. et al. // Int. J. Hydrogen Energy. 2015. V. 40. № 45. P. 15672. https://doi.org/10.1016/J.IJHYDENE.2015.09.059
  33. Raison P.E., Pavel C.C., Jardin R. et al. // Phys. Chem. Miner. 2010. V. 37. P. 555. https://doi.org/10.1007/s00269-010-0356-5
  34. Feng J., Xiao B., Zhou R. et al. // J. Appl. Phys. 2012. V. 111. P. 103535. https://doi.org/10.1063/1.4722174
  35. Qun-bo F., Feng Z., Fu-chi W. et al. // Comput. Mater. Sci. 2009. V. 46. № 3. P. 716. https://doi.org/10.1016/j.commatsci.2009.02.033
  36. Zhang Y., Zhang Z., Zhu X. et al. // Appl. Phys. A. 2013. V. 115. № 2. P. 661. https://doi.org/10.1007/s00339-013-7843-8
  37. Osman R.A.M., Maos N., West A.R. // J. Am. Ceram. Soc. 2012. V. 95. № 1. P. 296. https://doi.org/10.1111/j.1551-2916.2011.04779.x
  38. Valant M. // J. Am. Ceram. Soc. 2009. V. 92. № 4. P. 955. https://doi.org/10.1111/j.1551-2916.2009.02984.x
  39. Cam D.P., Randall C.A., Shrout T.R. // Solid State Commun. 1996. V. 100. № 7. P. 529. https://doi.org/10.1016/0038-1098(96)00012-9

补充文件

附件文件
动作
1. JATS XML
下载

版权所有 © Russian Academy of Sciences, 2025

Согласие на обработку персональных данных с помощью сервиса «Яндекс.Метрика»

1. Я (далее – «Пользователь» или «Субъект персональных данных»), осуществляя использование сайта https://journals.rcsi.science/ (далее – «Сайт»), подтверждая свою полную дееспособность даю согласие на обработку персональных данных с использованием средств автоматизации Оператору - федеральному государственному бюджетному учреждению «Российский центр научной информации» (РЦНИ), далее – «Оператор», расположенному по адресу: 119991, г. Москва, Ленинский просп., д.32А, со следующими условиями.

2. Категории обрабатываемых данных: файлы «cookies» (куки-файлы). Файлы «cookie» – это небольшой текстовый файл, который веб-сервер может хранить в браузере Пользователя. Данные файлы веб-сервер загружает на устройство Пользователя при посещении им Сайта. При каждом следующем посещении Пользователем Сайта «cookie» файлы отправляются на Сайт Оператора. Данные файлы позволяют Сайту распознавать устройство Пользователя. Содержимое такого файла может как относиться, так и не относиться к персональным данным, в зависимости от того, содержит ли такой файл персональные данные или содержит обезличенные технические данные.

3. Цель обработки персональных данных: анализ пользовательской активности с помощью сервиса «Яндекс.Метрика».

4. Категории субъектов персональных данных: все Пользователи Сайта, которые дали согласие на обработку файлов «cookie».

5. Способы обработки: сбор, запись, систематизация, накопление, хранение, уточнение (обновление, изменение), извлечение, использование, передача (доступ, предоставление), блокирование, удаление, уничтожение персональных данных.

6. Срок обработки и хранения: до получения от Субъекта персональных данных требования о прекращении обработки/отзыва согласия.

7. Способ отзыва: заявление об отзыве в письменном виде путём его направления на адрес электронной почты Оператора: info@rcsi.science или путем письменного обращения по юридическому адресу: 119991, г. Москва, Ленинский просп., д.32А

8. Субъект персональных данных вправе запретить своему оборудованию прием этих данных или ограничить прием этих данных. При отказе от получения таких данных или при ограничении приема данных некоторые функции Сайта могут работать некорректно. Субъект персональных данных обязуется сам настроить свое оборудование таким способом, чтобы оно обеспечивало адекватный его желаниям режим работы и уровень защиты данных файлов «cookie», Оператор не предоставляет технологических и правовых консультаций на темы подобного характера.

9. Порядок уничтожения персональных данных при достижении цели их обработки или при наступлении иных законных оснований определяется Оператором в соответствии с законодательством Российской Федерации.

10. Я согласен/согласна квалифицировать в качестве своей простой электронной подписи под настоящим Согласием и под Политикой обработки персональных данных выполнение мною следующего действия на сайте: https://journals.rcsi.science/ нажатие мною на интерфейсе с текстом: «Сайт использует сервис «Яндекс.Метрика» (который использует файлы «cookie») на элемент с текстом «Принять и продолжить».